e-Beam and γ-rays Induced Synthesis and Catalytic Properties of Copper Nanoclusters-Deposited Composite Track-Etched Membranes

Показать сокращенную информацию

dc.contributor.author Parmanbek, Nursanat
dc.contributor.author Aimanova, Nurgulim A.
dc.contributor.author Mashentseva, Anastassiya A.
dc.contributor.author Barsbay, Murat
dc.contributor.author Abuova, Fatima U.
dc.contributor.author Nurpeisova, Dinara T.
dc.contributor.author Jakupova, Zhanar Ye.
dc.contributor.author Zdorovets, Maxim V.
dc.date.accessioned 2024-09-13T07:29:53Z
dc.date.available 2024-09-13T07:29:53Z
dc.date.issued 2023
dc.identifier.citation Parmanbek, N.; Aimanova, N.A.; Mashentseva, A.A.; Barsbay, M.; Abuova, F.U.; Nurpeisova, D.T.; Jakupova, Z.Y.; Zdorovets, M.V. e-Beam and γ-rays Induced Synthesis and Catalytic Properties of Copper Nanoclusters-Deposited Composite Track-Etched Membranes. Membranes 2023, 13, 659. https:// doi.org/10.3390/membranes13070659 ru
dc.identifier.issn 2077-0375
dc.identifier.other doi.org/10.3390/membranes13070659
dc.identifier.uri http://rep.enu.kz/handle/enu/16309
dc.description.abstract Effective removal of toxic inorganic and organic pollutants is one of the current leading challenges of wastewater treatment. In this study, the decomposition of methylene blue (MB) under UV light irradiation was investigated in the presence of copper nanoclusters (NCs)-deposited polyethylene terephthalate (PET) track-etched hybrid membranes. PET track-etched membranes (TeMs) with an average pore size of ~400 nm were grafted by functional acrylic acid (AA) monomer under electron beam irradiation after oxidation with H2O2/UV system. The radiation dose varied between 46 and 200 kGy. For the deposition of copper NCs, poly(acrylic acid) (PAA)-grafted membranes saturated with Cu(II) ions were irradiated either by electron beam or γ-rays to obtain copper-based NCs for the catalytic degradation of MB. Irradiation to 100 kGy with accelerated electrons resulted in the formation of small and uniform copper hydroxide (Cu(OH)2 ) nanoparticles homogeneously distributed over the entire volume of the template. On the other hand, irradiation under γ-rays yielded composites with copper NCs with a high degree of crystallinity. However, the size of the deposited NCs obtained by γ-irradiation was not uniform. Nanoparticles with the highest uniformity were obtained at 150 kGy dose. Detailed analysis by X-ray diffraction (XRD) and scanning electron microscopy (SEM) confirmed the loading of copper nanoparticles with an average size of 100 nm on the inner walls of nanochannels and on the surface of PET TeMs. Under UV light irradiation, composite membranes loaded with NCs exhibited high photocatalytic activity. It was determined that the highest catalytic activity was observed in the presence of Cu(OH)2@PET-g-PAA membrane obtained at 250 kGy. More than 91.9% of the initial dye was degraded when this hybrid membrane was employed for 180 min, while only 83.9% of MB was degraded under UV light using Cu@PETg-PAA membrane. Cu(OH)2@PET-g-PAA membranes obtained under electron beam irradiation demonstrated a higher photocatalytic activity compared to Cu@PET-g-PAA membranes attained by γ-rays. ru
dc.language.iso en ru
dc.publisher Membranes ru
dc.relation.ispartofseries Volume 13;Issue 7
dc.subject track-etched membranes ru
dc.subject radiation-induced grafting ru
dc.subject accelerated electrons ru
dc.subject copper nanoclusters ru
dc.subject methylene blue degradation ru
dc.title e-Beam and γ-rays Induced Synthesis and Catalytic Properties of Copper Nanoclusters-Deposited Composite Track-Etched Membranes ru
dc.type Article ru